Method of producing ribbed board and product thereof

ABSTRACT

A method for the production of ribbed board product, such as fiberboard or flakeboard, which resists fracturing during manufacture. The ribbed board product made according to the invention can be used as decking in packaging components.

This application claims the benefit under 35 U.S.C. §119(e) of provisional application Ser. No. 60/108,088 filed Nov. 12, 1998.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates generally to composite articles. More specifically, the invention relates to a method of producing molded board products useful for packaging components.

2. Description of Related Technology

Many types of wood composites exist, including, for example: fiberboards such as hardboard, medium density fiberboard, and softboard; chipboards such as particleboard, waferboard; and oriented strandboard. Boards made of combinations of these materials are also useful.

Many different methods of manufacturing these wood composites such as fiberboard are known in the art, for example as disclosed in U.S. Pat. No. 4,514,532 (Apr. 30, 1985) to Hsu et al. and U.S. Pat. No. 4,828,643 (May 9, 1989) to Newman et al. The disclosures of these patents are incorporated herein by reference. The principal processes for the manufacture of fiberboard include (a) wet felted/wet pressed or “wet” processes, (b) dry felted/dry pressed or “dry” processes, and (c) wet felted/dry pressed or “wet-dry” processes. Synthetic resins, such as phenol-formaldehyde (“PF”) resins or modified PF resins, are often used as binders in these processes.

Generally, in a wet process, cellulosic fibers (e.g., woody chip material subjected to fiberization in a pressurized refiner to form wood fibers) are blended in a vessel with large amounts of water to form a slurry. The slurry preferably has sufficient water content to suspend a majority of the wood fibers and preferably has a water content of at least 95 percent by weight (“weight percent”). The water is used to distribute a synthetic resin binder, such as a phenol-formaldehyde resin over the wood fibers. This mixture is deposited onto a water-pervious support member, such as a fine screen or a Fourdrinier wire, and precompressed, whereby much of the water is removed to leave a wet mat of cellulosic material having, for example, a moisture content of about fifty percent, based on the weight of dry cellulosic material. The wet mat is transferred to a press and consolidated under heat and pressure to form the molded wood composite.

A wet-dry forming process can also be used to produce wood composites. Preferably, a wet-dry process begins by blending cellulosic material (e.g., wood fiber) in a vessel with a large amount of water. This slurry is then blended with a resin binder. The blend is then deposited onto a water-pervious support member, where a large percentage (e.g., 50 weight percent or more) of the water is removed, thereby leaving a wet mat of cellulosic material having a water content of about 40 wt. % to about 60 wt. %, for example. This wet mat is then transferred to a zone where much of the remaining water is removed by evaporation by heat to form a dried mat. The dried mat preferably has a moisture content of about 10 wt. % or less. The dried mat is then transferred to a press and consolidated under heat and pressure to form a wood composite which may be a flat board or a molded product, for example. The product can be molded into various shapes or geometries depending on the intended use.

In a dry process, the wood fibers are generally conveyed in an airstream or by mechanical means, rather than by a liquid stream. Wood fibers supplied from a fiberizing apparatus are blended with a thermosetting resin binder, such as a phenol-formaldehyde resin, and a sizing agent such as wax. The fibers with an addition of resin (3-10%) and wax can be dried and then be randomly formed into a mat (felted) by air blowing the fibers onto a support member. The mat, typically having a moisture content of about 5-8 wt. % based on the weight of dry fibers, is then pressed under heat and pressure to cure the thermosetting resin and to compress the mat into an integral consolidated structure. This mat can be pressed into various shapes varying from flat panel to three-dimensional using machined die sets.

When pressing mats into a ribbed configuration, however, various problems may arise. When creating ribbed high density fiberboard, fracturing of the board can occur at the flats of the ribbed configuration, reducing the strength and handleability of the product. Other problems may include a soft surface, lack of consolidation, brittleness, blistering, and warping in the final product.

It would therefore be desirable to be able to manufacture a ribbed high density fiberboard that does not fracture during manufacturing.

The present application is also directed to the production of packaging components such as pallets. Pallets are currently made from a variety of different materials such as wood, plywood, wood composites, plastic, corrugated card board, and metal. These materials each have their own distinct advantages and disadvantages. Solid wood remains the most common material used in pallets because of its lower cost, strength, and stiffness. Wood, however, is inconsistent, heavy when wet, and requires a great deal of labor when assembling into pallets. Plywood pallets are known for their long life expectancy of seven to eight years. In addition, they are easy to repair. However, plywood may be heavy. Furthermore, it may be more expensive, because it must be cut from a four foot by eight foot panels, which causes a lower yield per panel.

Plastic pallets, including those made of high density polyethylene, have also been used. However, they can be four times more expensive than wood pallets. Advantages of plastic pallets are moldability and cleanability. Sag resistance, fire threats, and difficult repairability are known limiting factors.

Metal pallets are used by the smallest segment of the industry. They are very expensive, however, they can hold large loads, are virtually indestructible.

Wood/plastic composite pallets, such as those available from Dura Products International of Toronto, Ontario and Litco International Inc. of Vienna, Ohio can be made from sawdust shavings and waste plastic bottles. Wood composite pallets are lighter than wood, fully recyclable, economically competitive, and have consistent dimensions. The weaknesses of composite pallet products include rackability, which is limited to 2800 pounds. Further, if some types of wood/plastic composite products are exposed to fire, they can emit toxic fumes.

Corrugated pallets are single-use items, and are limited to a 500-2800 pound weight limit. The advantages of corrugated material include recyclability and design flexibility. These pallets are safe for the worker to handle, are easy to dispose of, produce no splinters, use no nails, have product uniformity free of mold spores, and are one-third the weight of wood. However, corrugated pallets are more easily damaged than wood, difficult to use on conveyor systems, weight restricted, and will degrade in the presence of water. Corrugated pallets can be wax-coated so as to delay water damage. However, when such products are wax-coated, they become more expensive and difficult to recycle.

It would therefore be desirable to manufacture a pallet that retains the beneficial properties of corrugated pallets while increasing its water resistance and strength attributes.

SUMMARY OF THE INVENTION

It is an object of the invention to overcome at least one of the problems described above.

According to the invention, a mat including material such as wood-based materials, agricultural fibers, and synthetic fibers and a binder resin is provided in a die configured to produce a ribbed composite board having contiguous outer zones and angled zones. The die is configured to produce a caliper difference between the outer zones and the angled zones, preferably wherein the outer zones have a caliper less than the angled zones.

According to an embodiment of the invention, a packaging component, such as a pallet deck or pallet strips, incorporates the ribbed composite board of the invention.

Other objects and advantages of the invention will become apparent to those skilled in the art from the following detailed description, taken in conjunction with the drawings and the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1(a) is a cross-sectional view of a die set used according to the invention.

FIG. 1(b) is a cross-sectional view of the ribbed board product produced according to the invention.

FIG. 2(a) is a cross-sectional view of a preferred embodiment of the ribbed board product produced according to the invention.

FIG. 2(b) is a cross-sectional view of a die set used according to a preferred embodiment of the invention.

FIG. 3(a) is a top view of a die set used according to a preferred embodiment of the invention.

FIG. 3(b) is a top view of a preferred embodiment of a ribbed board product produced according to the invention.

FIG. 4 is a perspective view of a ribbed board product produced according to the invention.

FIG. 5 is a perspective view of a waffle-shaped ribbed board product produced according to the invention.

FIG. 6 is a perspective view of a multi-directional ribbed board product produced according to the invention.

FIG. 7 is a perspective view of a ribbed board product produced according to the invention.

FIG. 8 is a perspective view of a pallet including a ribbed board product produced according to the invention.

FIG. 9 is a perspective view of a pallet including a ribbed board product produced according to the invention.

DETAILED DESCRIPTION OF THE INVENTION

According to the present invention, a method is provided for producing a ribbed composite product from a mat including materials such as wood-based materials, agricultural fibers, and synthetic fibers. The wood-based materials may include fibers, flakes, and/or wafers. In addition, the mat may include fillers as well, to achieve various desired properties. According to this method, the mat is consolidated under heat and pressure in an apparatus configured to produce a ribbed composite board material, such as fiberboard, flakeboard, or waferboard. Upon pressing, the board retains integrity and does not fracture. The ribbed molded composite products of the invention further have increased stiffness and handleability in the ribbed direction over its corresponding panel products. The advantageous properties of the inventive product allow it to be an excellent component in applications such as pallet decking, pallet strips, slip sheets, inserts for corrugated boxes, and outside protective packaging.

An example of producing a preferred ribbed high density fiberboard product is described below. However, it is to be understood that the invention is also applicable to the production of other ribbed wood composite products, including flakeboards, waferboard, oriented strandboard, or fiberboards, for example. A preferred ribbed product of the invention is made from a raw material obtained by breaking down logs or other source of wood into chips. The chips are is then refined in thermo-mechanical refiners that break down the chips into relatively uniform fibers by using steam and mechanical action. (Wood flakes, used in the inventive flakeboard product, are produced through mechanical slicing and flaking.) The source of fiber for the inventive wood composite product is preferably mixed hardwood or softwood species, but the raw material may also be agricultural based fibers (such as straw fiber, kenaf fiber, and hemp fiber) or synthetic fibers. The fibers used depend upon availability, cost, and special use requirements. Various methods of producing these fibers are known in the art.

The ribbed high density fiberboard of the invention is preferably formed using a dry felted process. Dry felted processes are disclosed in “Fiberboard Manufacturing Practices in the United States” by Otto Suchsland et al., U.S. Department of Agriculture, 1986, the disclosure of which is hereby incorporated herein by reference. In the dry process of the invention, the wood fibers are preferably conveyed in an airstream or by mechanical means, rather than by a liquid stream. However, the inventive method may also use a wet or a wet-dry process known in the art. Wood fibers supplied from a fiberizing apparatus can be added with a thermosetting resin binder in a mixing procedure with blow line or blender processes. Phenol-formaldehyde (“PF”) and melamine-urea-formaldehyde (“MUF”) resins are preferred, but other resins known in the art, such as isocyanate resins, may be used. As an example, PF resin may be added at about 1% to about 8%, more preferably about 3.5% to about 4.5%, based on the weight of the dry fibers. Wax, such as an emulsified wax, is also preferably added to the wood fibers to improve water resistance of the final product, preferably at a rate of about 1.0% to about 2.5%, based on the weight of the dry fibers. A tempering oil may also be applied to the face of the final product to improve surface hardness, machineability, and water resistance of the final product.

The resin-blended fibers preferably are dried and then randomly formed into a continuous mat by air blowing the fibers onto a support member. The continuous mat, typically having a moisture content of about 5% to about 10% based on the weight of dry fibers with a preferred moisture content of about 5.5% to 7 % based on the weight of dry fibers, is then consolidated under heat and pressure to cure the thermosetting resin and to compress the mat into a consolidated product or integral structure.

As will be apparent to those of skill in the art, desirable pressing temperatures and pressures may be modified according to various factors, including the following: the thickness of the board, the type of fiber/flakes being pressed, the moisture content of the raw material, the press time, and the type of resin that is utilized. The moisture content of the wood-based materials and/or agricultural fibers (known as “furnish moisture content”) is one important factor which controls the core temperature of the mat that can be achieved under given press conditions and therefore may control the press cycle. Press time can be decreased by increasing press temperature.

According to the present invention, the mat is placed in a die set with a preferred unique design. The die set has a configuration, described in greater detail below, that allows for the production of a ribbed article, preferably having (a) both multiple generally planar longitudinally extending outer zones (sometimes referred to as flat zones or raised zones) and (b) multiple longitudinally extending inner zones (sometimes referred to as angled zones or sloped zones) that are disposed between and contiguous with the outer zones. These configurations will be described in more detail in conjunction with the drawings.

Referring initially to FIG. 1(a), the substrate caliper of a final board product will be defined by the distance or gap left during pressing of a mat between a first die 9 and a second die 10. (The die set is referred to generally as element 40.) For example, a substrate caliper at one point of a product produced by the die set 40 will be defined by the distance or gap between point A and point B in FIG. 1(a) when the die set 40 is closed during consolidation. As described in detail below, the product produced by the die set 40 will preferably have a caliper and density that differs in at least two locations in the product.

A product 8 of the invention produced by the die set 40 of FIG. 1(a) is exemplified in FIG. 1(b) and FIG. 4. The product 8 shown in FIG. 1(b) has (a) multiple generally planar longitudinally extending outer zones 11 and (b) multiple longitudinally extending inner or angled zones 12 that are disposed between and contiguous with the outer zones 11. The outer zones 11 may be disposed either upwardly of (e.g., elements 11 a, 11 b, 11 c in FIG. 1(b)) or downwardly of (e.g., elements 11 d, 11 e, 11 f) and contiguous with the angled zones 12. Adjacent outer zones (e.g., zones 11 a and 11 d) are spaced apart laterally a predetermined distance and vertically a predetermined distance. The outer zones 11 a, 11 b, 11 c disposed upwardly (as shown in FIG. 1(b)) from the angled zones 12 may have a width either equal to or different from the width of the outer zones 11 d, 11 e, 11 f if disposed downwardly from the angled zones 12. While the outer zones 11 shown in FIG. 1(b) are generally flat (planar), in some cases the outer zones 11 may have contours. For example, a subtle texture or other contour may be added to the outer zones of the product, to provide improved surface friction. Therefore, the use of the term flat herein refers to a generally planar portion. An outer zone 11 may also be formed by the peak of a curved portion of the product 8. For example, a product may have a cross section in the shape of a sinusoidal curve.

The angled zones 12 can form various angles with the outer zones 11. These draft angles may vary from about zero degrees to about 90 degrees, and preferably between about 30 degrees and about 90 degrees.

As the result of differing die gaps, the die set 40 of the invention will preferably produce a product 8 having a density and caliper that vary from one point to another. In general, the caliper of the outer zones 11 will be less than (thinner than) the caliper of the product 8 at the angled zones 12. (The caliper of the outer zones 11 a, 11 b, 11 c may be different than the caliper of the outer zones 11 d, 11 e, 11 f.) The differing caliper will provide substantial and unexpected advantages in production and use of the board product 8.

The caliper of the board 8, the distance between point A and point B in FIG. 1(b), generally may vary between about 0.085 inch to about 0.5 inch (about 2.16 mm to about 12.7 mm). The caliper of the angled zones 12 preferably differs (e.g., is greater than) from that of the outer zones 11. In fact, the ratio of the caliper of the outer zone to the caliper of the angled zone is less than 1.0, and preferably less than 0.9. For example, the caliper of the angled zones 12 is preferably in a range of about 0.115 inch to about 0.140 inch (about 2.92 mm to about 3.56 mm), with about 0.125 inches to about 0.130 inches (about 3.18 mm to about 3.30 mm) being preferred. The caliper of the outer zones 11 preferably is in a range of 0.09 inch to 0.115 inches (about 2.29 mm to about 2.93 mm) with a caliper of about 0.10 inch to about 0.115 inch (about 2.54 mm to about 2.92 mm) being preferred.

The molded rib product according to the invention has an overall specific gravity of 0.6 to 1.10. The molded rib hardboard product preferably has an overall specific gravity of about 0.80 or greater, and more preferably is in a range of about 0.80 to about 1.10, depending upon the end use of the product, making the product a high density wood composite. The inventive flakeboard molded rib product preferably has an overall specific gravity of about 0.50 or greater, and more preferably in a range of about 0.60 to about 0.90. The invention may produce a fiberboard with a density of at least about 45 lb/ft³ , for example in a range of about 45 lb/ft³ to about 60 lb/ft³ (about 0.73 g/cm³ to about 0.96 g/cm³).

According to the invention, in the fiberboard product, the outer zone 11 may have a specific gravity of about 0.90 to about 1.10, preferably about 0.95 to about 1.05, with about 0.98 to about 1.02 being most preferred. The angled zone 12 may have a specific gravity of about 0.80 to about 0.90, preferably about 0.80 to about 0.87, with about 0.82 to about 0.86 being most preferred.

The profile thickness of the product (measured by the greatest depth of the product, for example, the distance from a top surface of zone 11 a to a bottom surface of zone 11 d) may vary in a range of about 0.25 inches to about 1.5 inches (about 6.35 mm to about 38.1 mm), with about 0.350 inches to about 0.750 inches (about 8.89 mm to about 19.05 mm) being preferred.

The depth of draw in the final product 8 may also be an important parameter for some applications. The depth of draw, the distance between the outer zones, is measured as the vertical distance traveled by an angled zone 12 between adjacent outer zones (e.g., the zones 11 a and 11 d). While the depth of draw may be uniform throughout a ribbed product 8, this need not be the case. Thus, the top surfaces of the outer zones 11 are optionally in a single plane. The depth of draw may be in a range of about 0.125 inch to about 1.0 inch (about 3.1 mm to about 25.4 mm).

Referring to FIGS. 2(a) and 3(a), a board product 15 may also be produced with relatively low density areas or buttons 13 protruding from an upper surface or face 14 of the outer zones 11 of the rib profile. These low density buttons 13 preferably are debossed pads that extend about 0.030 inches to about 0.090 inches (about 0.76 mm to about 2.3 mm) (e.g., approximately 0.060 inches) (about 0.15 cm) upwardly from the top face 14 of the generally planar outer zones 11, and preferably are approximately 0.093 inches to 0.312 inches (about 2.3 mm to about 7.9 mm) in diameter, with about 0.093 inches to 0.125 inches (about 2.3 mm to about 3.2 mm) in diameter being preferred. The buttons 13 provide an integrated cushion for items placed on the ribbed hard density fiberboard or flakeboard. A typical application with the buttons may involve use of the product as drop-in sheets or slip sheets in corrugated box containers.

FIG. 2(b) shows a die set 41 for producing the product 15, including a first die 20 and a second die 21. Both the first die 20 and the second die 21 have cavities 22 along with a configuration for producing outer zones 11 and angled zones 12. FIG. 3(b) shows a top view of the die 20 having the cavities 22. As described above, a mat is produced from wood fiber material and placed between the first die 20 and the second die 21. During the consolidation stage, this die configuration permits these lower density cavities 22 to create low density buttons 13 on the outer zones 11 of the ribbed high density fiberboard, as shown in FIGS. 2(b) and 3(b).

The geometrics of the die and its product are not limited to a single ribbed configuration as shown in FIGS. 14. The die may further include repetitive pattern single and multiple direction ribbing to variable depths and draft angles. For example, the die set 40 may be configured to produce a chevron-shaped or waffle-shaped ribbed board, as shown in FIGS. 7 and 5, respectively, or the die set may be configured to produce multiple direction ribbing as shown in FIG. 6. Like elements from FIGS. 1-4 are shown with the same reference numerals in FIGS. 5-7. Another alternative approach includes laminating multiple plies of ribbed decks or strips together.

The ribbed boards of the invention provide unexpected results in a unique combination of properties in a single material, including a combination of cushioning characteristics and structural properties. The cushioning characteristics of the inventive boards provide increased ability to absorb high impact energy. The control of geometry with molded wood composites can provide three separate types of cushioning. First, as described above, there can be localized low density areas 13 on the outer side of the outer zones 11 of the rib profile. Further, compression from the deflection of the rib geometry itself can provide additional cushioning. Finally, there is also localized compression in the angled zone 12 of the profile caused by the above-described density gradient between the higher density outer zone 11 against the lower density angled zones 12 in the rib profile. This will be particularly desirable for products of a fragile nature. Specialty coatings could be applied to the surface of the ribbed panel to provide added performance such as fire protection.

The particular profile geometry produced according to this invention controls the density at specific locations in the outer zones 11 and angled zones 12 of the rib configuration. This not only maximizes its stiffness properties of the final product, but it also maintains the integrity of the wood composite during compression. A mat may be stretched as much as 30% or slightly more in an out-of-plane direction during pressing without fracturing occurring at the outer zones 12, whereas when conventional rib dies (having a uniform caliper) are used, the mat typically fractures when a stretching of 15% to 16% occurs.

Factors influencing the amount a mat can stretch during pressing with the invention include the size of the ribs or corrugations; the variation of density in the outer and angled zones of the final profiles after pressing; the bulk density and orientation of the composite materials such as oriented strand board (OSB) prior to press closure; and the fiber and flake geometry (including physical size, length, width and thickness of resource materials), which affect the ability of the wood composite to shift or slide within the matrix of the mat before bypassing, fracturing or destroying the continuity of the composite mat during press closure. The process used as well as the unique die design used according to the invention helps to manipulate these stretching factors so that the mat may stretch up to 30% without fracturing the mat at the outer zone 12.

Table 1 shows the compressive properties of the ribbed high density fiberboard made according to the invention. Maximum loads, maximum stress displacement at maximum load, and the percent strain at the maximum load were measured during compressive testing. These values depend on various factors including rib width, depth of draw, transition radius, severity of angle, the number of ribs per unit of width, and whether the ribs were restrained from the outer perimeter to the center of the sample. It was found that a rib width of 1.179 inches (about 3 cm) allowed for a maximum load of 3301 pounds and a maximum stress of 188.5 psi. The displacement of the board at maximum load was 0.087 inches (2.2 mm), while the percent strain at maximum load was 24.2%.

TABLE 1 Actual Dis % Rib Load Load place- Strain Load Bearing at Stress at at Rib Ribs Bearing Sample Max at Max Rib Max. Max. Width per Re- Area Area Load Load Height Load Load (in.) Sample strained (in.²) (in.²) (lbs.) (psi) (in.) (in.) (%) 1.179 1 Yes 3.588878 4.16 297.6 71.5 0.36 0.173 48.1 1.179 1 Yes 3.578265 3.89 311.6 80 0.36 0.158 43.9 1.179 1 Yes 3.585339 4.14 286.1 89.1 0.36 0.165 45.8 1.179 3 No 10.702962 10.65 858.2 80.5 0.36 0.052 14.4 1.179 3 No 10.593315 10.68 691.9 83.5 0.36 0.056 15.6 1.179 3 No 10.699425 10.74 685.6 63.9 0.36 0.046 12.8 1.179 3 Yes 8.93 9.13 1284 138.4 0.36 0.088 24.4 1.179 3 Yes 10.72 10.92 1610 147.5 0.36 0.103 28.6 1.179 3 Yes 9.08 9.32 1393 149.4 0.36 0.095 26.4 1.179 3 Yes 10.76 18.25 2152 117.9 0.36 0.082 22.8 1.179 3 Yes 10.65 17.66 1934 109.5 0.36 0.085 23.6 1.179 3 Yes 10.98 17.35 2149 123.9 0.36 0.076 21.1 1.179 5 No 17.950275 17.94 1318 73.5 0.36 0.048 13.3 1.179 5 No 17.93259 18.16 1894 104.3 0.36 0.05 13.9 1.179 5 No 17.808795 18.03 1753 97.2 0.36 0.059 16.4 1.179 5 Yes 17.43 17.71 2873 162.3 0.36 0.089 24.7 1.179 5 Yes 17.31 17.51 3301 188.5 0.36 0.087 24.2 1.197 3 Yes 10.59 11.34 1362 120.1 0.375 0.084 22.4 1.197 3 Yes 10.81 11.97 1204 100.6 0.375 0.082 21.9 1.197 3 Yes 10.69 11.36 1327 116.9 0.375 0.099 26.4 1.197 3 Yes 10.83 11.62 1513 130.2 0.375 0.066 22.9 1.197 3 Yes 10.83 11.52 1549 134.5 0.375 0.089 23.7 1.375 3 Yes 12.16 12.84 1536 119.6 0.391 0.099 25.3 1.375 3 Yes 12.21 12.51 1154 92.2 0.391 0.09 23 1.375 3 Yes 12.19 12.53 1596 127.3 0.391 0.087 22.3 1.375 3 Yes 12.27 12.54 1379 110 0.391 0.102 26.1 1.375 3 Yes 12.37 12.62 1129 89.4 0.391 0.096 24.6 1.25 3 Yes 11.01 11.76 1439 122.4 0.391 0.121 30.9 1.25 3 Yes 11.25 11.98 1312 109.6 0.391 0.089 22.8 1.25 3 Yes 11.31 11.91 1335 112.1 0.391 0.098 25.1 1.25 3 Yes 11.10 11.77 1084 92.1 0.391 0.092 23.5 1.25 3 Yes 11.18 11.79 1232 104.5 0.391 0.096 24.6

Table 2 shows the stiffness properties of the ribbed board of the invention. Six samples of the invention, all measuring 6 inches in width and spanning 10 inches in length were subjected to testing to determine various strength properties. The results are shown in Tables 2 below.

TABLE 2 Modulus Stiffness/ Rib Rib of Modulus of Stiffness Break Sample Sample Ribs Width Height Rupture Elasticity × Span (lb.- Load Width Width per (in.) (in.) (psi) 1000 psi (in.) in.{circumflex over ( )}2) (lbs.) (lb.-in.) (in.) Sample 1.179 0.36 1667 161 10 3754 86.4 626 6 5 1.179 0.36 1929 190 10 4411 100 735 6 5 1.179 0.36 2226 201 10 4658 115.4 776 6 5 1.25 0.391 1800 171 10 5041 110.1 840 6 5 1.25 0.391 1810 175 10 5137 110.7 856 6 5 1.25 0.391 1802 180 10 5282 110.2 880 6 5

Table 3 shows a comparison of the average stiffness of board produced according to the invention with different rib widths to the average stiffness of ¼inch (6.35 mm) thick high density fiberboard.

TABLE 3 Average Stiffness/Sample Width Description (lb.-in.) ¼″ High Density Fiberboard 593.583 Rib Width of 1.179 in. 712.333 Rib Width of 1.25 in. 858.667

In addition to improved strength and stiffness properties, the ribbed board produced according to the invention is that the upper and lower surfaces 14 of the ribbed hardboard (the outer surface of outer zones 11) may provide a uniform plane with consistent texture or smoothness, unlike natural wood which typically has knots, splits, and/or cracks due to the prevalent use of “green” high moisture lumber. Because of this uniform plane, there is an equal weight distribution of any product placed on the ribbed high density fiberboard or flakeboard, for example. Thus, the ribbed high density products of the invention are less likely to fracture or cause damage from localized pressure points. Conversely, when a load is placed on a non-consistent surface such as wood, pressure points develop creating stress and possibly fractures on the pallet material as well as materials being shipped on the pallet.

The surfaces 11, 14, or 16 may also be tempered to add hardness or glueability to these surfaces. Further, the molded rib panels may be laminated together or with alternate materials to achieve low weight components for higher stiffness and compressive properties, for example, in pallets and shipping applications.

This process according to the invention produces a single component material that integrates an engineered combination of various desired properties useful in packaging components such as, compressive strength, stiffness, impact deflection, variable shock absorption, an increased water repellency over corrugated paper pallets, and surface friction when steel die surface is textured. These properties in combination are unique to fiberboard and flakeboard because within the described process of low resin usage, the furnish does not flow during pressing formation, thus creating the variable density which generates controllable physical properties of stiffness and/or compressive attributes in a single component. This change in density also facilitates breathing of steam inherent in the process at higher than normal density zone as defined by the rib profile caliper changes. This feature differs from other wood composite pallets which use higher resin and wood particles to achieve uniform density throughout their products.

Through the manipulation of die geometry, a balance between compressive strength, cushioning properties, and flexural stiffness is achieved. Fiberboard or flakeboard produced according to the invention makes it an excellent material for use in packaging components, such as decks and strips for shipping and storage pallets. FIGS. 7 and 8 illustrate pallets 50 and 51 produced from the inventive hardboard/flakeboard material. A deck 44 (FIG. 7) or strips 45 (FIG. 8) cut from this ribbed high density fiberboard/flakeboard are fastened to support runners 46 by known methods including staples, nails, and adhesives. The support runners 46 may be made from wood composite materials, or low grade aspen or oak lumber that is not kiln dried. Further, paper, flat hardboard (for example, a commercial lightweight laminate panel produced by Masonite Corp.) or other flat sheet materials can be laminated (not shown) and may be used on the pallet deck to stiffen the component on one or both sides of the ribbed panel.

Products made according to this invention such as packaging components or pallets exhibit many improved attributes. First, the invention allows for control of the surface density of the pallet. A panel that is more dimensionally stable versus “green” lumber with higher moisture content and provides an improved planar surface than whole wood lumber is preferably utilized, which provides a uniform medium for nails and staple penetration and jacking resistance. Second, the product possesses significantly higher compression strength and stiffness than corrugated paperboard. Third, the invention can provide a product with sufficient surface friction to avoid slippage of materials placed thereon. Fourth, the pallets also provide cushioning that absorbs live load impact shock. Fifth, the design also provides resistance to damage caused by fork lifts or other machinery used to move the pallets. This design prevents full deck failure by limiting damage to a localized edge, sacrificing one or two ribs. Sixth, a deck made from the inventive material itself is a conveyable material, which provides a slip-sheet or carrier for products during in-house operations, and a separator sheet for products being warehoused. Seventh, the product is environmentally friendly and can be ground up and easily disposed of or reused, unlike plastics and foams that often involve landfilling. Eighth, the product panel is lightweight relative to whole lumber products, and nests or stacks in less space, assembles easily and results in a consistent, high yield usage in field application. Finally, the inherent nature of the ribbed profile ribbing design allows nails and/or fasteners to be recessed below the flat plane of the ribs.

The foregoing description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom, as modifications within the scope of the invention will be apparent to those skilled in the art. 

What is claimed is:
 1. A method of producing a ribbed board product, said method comprising the steps of: a) forming a mat comprising a material selected from the group consisting of wood-based materials, agricultural fibers, and synthetic fibers; b) providing the mat in a die, said die having a ribbed configuration with at least two spaced apart outer zones and at least two angled zones; c) closing the die to form a die gap, wherein the die gap at said at least two spaced apart outer zones differs from the die gap at said at least two angled zones; and wherein the die gap of each of said at least two spaced apart outer zones includes a cavity to provide low density areas on said at least two spaced part outer zones; and d) consolidating said mat under pressure and heat to form the ribbed board product having said low density areas on the outer zones.
 2. The method of claim 1 wherein the die gap at the at least two outer zones during step d) is about 0.090 inch to about 0.115 inch.
 3. The method of claim 2 wherein the die gap at the at least two outer zones during step d) is about 0.1 inch to about 0.115 inch.
 4. The method of claim 1 wherein the die gap at the at least two angled zones during step d) is about 0.115 inch to about 0.140 inch.
 5. The method of claim 1 wherein the die gap at the at least two angled zones during step d) is about 0.125 inch to about 0.130 inch.
 6. The method of claim 1 wherein the product has a draft angle of from about 30 degrees to about 90 degrees.
 7. The method of claim 1 wherein the material comprises wood fiber and step d) comprises consolidating the mat to a board having an overall specific gravity of about 0.80 to about 1.10.
 8. The method of claim 1 wherein the material comprises wood flakes and step d) comprises consolidating the mat to a board having an overall specific gravity of about 0.60 to about 0.90.
 9. The method of claim 1 wherein step d) comprises consolidating the mat to a board having a specific gravity at the outer zones of about 0.90 to about 1.10.
 10. The method of claim 1 wherein step d) comprises consolidating the mat to a board having a specific gravity at the angled zones of about 0.80 to about 0.90.
 11. The method of claim 1 wherein the ribbed board has a depth of draw of from about 0.125 inches to about 1.0 inches.
 12. The method of claim 1 wherein the outer surfaces of the outer zones lie in a single plane. 